SUS201 Stainless Steel Oval Bar
Product information
No.: SUS201(1Cr17Mn6Ni5N)
Executive standard: GB/T 1220-1992
Chemical composition:
| C | Si | Mn | P | Cr |
| 0.15 | 1.0 | 5.5-7.5 | 0.030 | 16.00~18.00 |
| Ni | N | |||
| 3.5-5.5 | 0.25 |
Product Usage:
Petroleum, electronics, chemical, pharmaceutical, textile, food, machinery, construction, nuclear power, aerospace, military and other industries!
Processing process:
Heat treatment specification: solid solution 1010 ~ 1120 ° C rapid cooling;
Microstructure:
The tissue characteristics are austenitic.
Theoretical weight table (unit: mm): diameter * diameter * 0.00623 = M / kg
Sizes
Unit (mm)
| Φ1.0 | Φ18 |
| Φ2.0 | Φ20 |
| Φ2.5 | Φ22 |
| Φ3.0 | Φ24 |
| Φ3.5 | Φ25 |
| Φ4.0 | Φ28 |
| Φ10.0 | Φ30 |
| Φ5.0 | Φ32 |
| Φ5.5 | Φ35 |
| Φ6.0 | Φ36 |
| Φ7.0 | Φ38 |
| Φ9.0 | Φ40 |
| Φ12 | Φ45 |
| Φ14 | Φ50 |
| Φ15 | Φ55 |
| Φ16 | Φ80 |
SUS304 Stainless Steel Oval Bar
Chemical composition:
| C | Si | Mn | P | Cr |
| 0.07 | 1.0 | 2.0 | 0.035 | 17.00~19.00 |
| Ni | S | |||
| 8.00-11.00 | 0.30 |
Product use:
petroleum, electronics, chemical, pharmaceutical, textile, food, machinery, construction, nuclear power, aerospace, military and other industries.
Processing process:
Yield strength (N/mm2) ≥ 205
Tensile strength ≥520
Elongation (%) ≥ 40
Hardness HB ≤187 HRB≤90 HV ≤200
Density 7.93 g•cm-3
Specific heat c (20 ° C) 0.502 J • (g • C) -1
Resistivity 0.73 Ω•mm2•m-1
Melting point 1398～1420°C
Theoretical weight table (unit: mm): length * width * thickness * 0.00793 / 1000 = kg
Sizes
| Φ1.0 | Φ18 |
| Φ2.0 | Φ20 |
| Φ2.5 | Φ22 |
| Φ3.0 | Φ24 |
| Φ3.5 | Φ25 |
| Φ4.0 | Φ28 |
| Φ10.0 | Φ30 |
| Φ5.0 | Φ32 |
| Φ5.5 | Φ35 |
| Φ6.0 | Φ36 |
| Φ7.0 | Φ38 |
| Φ9.0 | Φ40 |
| Φ12 | Φ45 |
| Φ14 | Φ50 |
| Φ15 | Φ55 |
| Φ16 | Φ80 |